Lithium/solid polymer electrolyte (SPE)/sulfur cells were studied in operando by two techniques: Scanning Electron Microscope (SEM) and ultraviolet-visible absorption spectroscopy (UV-vis). During the operation of the cell, extensive polysulfide dissolution in the solid polymer electrolyte (cross-linked polyethylene oxide) leads to the formation of a catholyte. A clear micrograph of the thick passivation layer on the sulfur-rich anode and the decreased SPE thickness by cycling confirmed the failure mechanism; the capacity decays by reducing the amount of active material, and by contributing to a charge inhibiting mechanism called polysulfide shuttle. The formation of elemental sulfur is clearly visible in real time during the charge process beyond 2.3 V. The non-destructive in operando UV-vis study also shows the presence of characteristic absorption peaks evolving with cycling, demonstrating the accumulation of various polysulfide species, and the predominant formation of S-4(2-) and of S-6(2-) during discharge and charge, respectively. This finding implies that the charge and discharge reactions are not completely reversible and proceed along different pathways. (C) 2016 Elsevier B.V. All rights reserved.