A simple fabrication method for preparation of surfaces able to switch from superhydrophobic to super hydrophilic state in a reversible and fast way is described. A self-assembled monolayer (SAM) consisting of quaternary ammonium group with aliphatic tail bearing terminal thiol functionality was created on gold nano/microstructured and gold planar surfaces, respectively. A rough nano/microstructured surface was prepared by galvanic reaction on a silicon wafer. The reversible counterion exchange on the rough surface resulted in a switchable contact angle between <5 degrees and 151 degrees. The prewetted rough surface with Cl- as a counterion possesses a superoleophobic underwater character. The kinetics of counterion exchanges suggests a long hydration process and strong electron ion pairing between quaternary ammonium group and perfluorooctanoate counterion. Moreover, a wettability gradient from superhydrophobic to superhydrophilic can be formed on the modified rough gold surface in a robust and simple way by passive incubation of the substrate in a counterion solution and controlled by ionic strength. Furthermore, adsorption of gold nanoparticles to modified plain gold surface can be controlled to a high extent by counterions present on the SAM layer.