Gelatin is alternatively adopted as the binder to modify Si anode coupling with its carbonization treatment. The binder can provide good bonding and uniform dispersion of the particles besides its environmental benignancy. Importantly, the carbonized binder containing nitrogen will be advantageous to the electrical conductivity of the electrode. In addition, some spaces are formed in the electrode due to the decomposition and shrinkage of the gelatin binder during heat-treatment, which may facilitate electrolyte penetration and accommodate volume change during cycling. All these merits make contribution to the good electrochemical performance of the modified Si electrode. It exhibits a reversible capacity of 990.3 mA h g(-1) after 70 cycles at a current density of 100 mA g(-1) and 904 mA h g(-1) after 100 cycles at 400 mA g(-1). (C) 2016 Elsevier B.V. All rights reserved.