We present the observation of transverse thermopower, or planar Nernst Effect (PNE), and planar Hall Effect (PHE) in patterned ultrathin film (similar to 8 nm) of La0.7Sr0.3MnO3 (LSMO). For PNE, a heat current was applied in-plane of the film (by creating a temperature gradient del T) whereas an in-plane current of 100 mu A was applied for measuring PHE. Even for a temperature difference of Delta T = 5 K the planar Nernst effect in LCMO ultrathin film (similar to 8 nm) shows a coercivity of similar to 3 Oe and confirms the ferromagnetic nature of the thin film. The angular dependence of transverse voltage in PNE shows a four-fold sin theta cos theta dependence symmetry at 250 K, which is consistent with the planar Hall effect measurement. (C) 2016 Elsevier B.V. All rights reserved.