A careful control of ZnO nanorod arrays with various densities and thickness were achieved by hydrothermal method. An obvious increase in the ZnO nanorod density is observed as the concentrations of zinc acetate dropped as expected through the surface SEM images. On the other hand, samples with and without TiO2 compact layer were also studied and results had been analyzed to seek for an optimized substrate structure for light absorbing layer and increase the efficiency. What's more, a deep research for the drying temperature for perovskite layer was also conducted. As a result, SEM images discribe a promising surface appearance of perovskite layer which is finely attached onto the nanorod structure. Final power conversion efficiency (PCE) of FTO/ZnO seed layer/ZnO nanorods/perovskite/spiro-OMe-TAD/Au electrode photovoltaic device reached similar to 9.15% together with open-circuit voltage of 957 mV, short-circuit current density of 17.8 mA/cm(2) and fill factor of 0.537. (C) 2016 Elsevier B.V. All rights reserved.