The PEDOT:PSS (poly(3,4-ethylenedioxythiophene):poly( styrenesulfonate)) was electrodeposited on a thin layer of bismuth vanadate (BiVO4) prepared using the pulsed laser deposition technique onto FTO. The inorganic-organic junction was characterized by Ramanspectroscopy, UV-vis spectroscopy and scanning electron microscopy. Chronoamperometry curves, recorded under simulated solar light illumination, were performed to determine generated photocurrent during water and hydroquinone oxidation at the electrode surface. Experiments were performed for three types of electrode materials: (i) FTO/BiVO4, (ii) FTO/PEDOT:PSS and (iii) FTO/BiVO4/PEDOT:PSS in aqueous electrolyte. Almost 5 times higher photocurrent in electrolyte containing hole scavenger was generated after modification of BiVO4 photoanode with electrodeposited polymer. It is noteworthy that anodic photocurrent was stable even after 4 h of illumination. Cyclic voltammetry curves of FTO/BiVO4/PEDOT:PSS recorded before and after experiments performed under electrode illumination indicated that the organic part in tested junction is photo-corrosion resistant. (C) 2016 Elsevier B.V. All rights reserved.