A thermally expanded graphene oxide (EGO) electrode is electrochemically activated to simultaneously introduce electrolyte-accessible mesopores and oxygen functional groups. The former is produced via O-2 evolution and the latter is incorporated by the intermediate hydroxyl radicals generated during the potentiostatic oxidation of H2O in 1 M H2SO4 at 1.2 V (vs. Ag/AgCl). When applied as a supercapacitor, the potentiostatically treated EGO (EGO-PS) shows significant enhancement in an electric-double layer (EDL) process with a noticeable Faradaic reaction and delivers high capacitance at fast charge/discharge (C/D) rates (334 F g(-1) at 0.1 A g(-1) and 230 F g(-1) at 50 A g(-1)). In contrast to EGO-PS, EGO that is oxidized potentiodynamically (EGO-PD) shows negligible enhancement in EDL currents. EGO that is subjected to successive potential pulses also shows behaviors similar to EGO-PD, which indicates the importance of hydroxyl radical accumulation via a potentiostatic method for simultaneous functionalization and microstructural control of graphenes. The potentiostatic post-treatment presented here is a convenient post-treatment strategy that could be used to readily increase capacitance and simultaneously improve the high-rate performance of carbon-based electrodes. (C) 2016 Elsevier B.V. All rights reserved.