Mixed tin (Sn)-lead-Pb) perovskites with high Sn content exhibit low bandgaps suitable for fabricating the bottom cell of perovskite-based tandem solar cells. In this work, we report on the fabrication of efficient mixed Sn-Pb perovskite solar cells using precursors combining formamidinium tin iodide (FASnI(3)) and methylammonium lead iodide (MAPbI-3). The best-performing cell fabricated using a (FASnI(3))(0.6)(MAPbI(3))(0.4) absorber with an absorption edge of similar to 1.2 eV achieved a power conversion efficiency (PCE) of 15.08 (15.00)% with an open-circuit voltage of 0.795 (0.799) V, a short-circuit current density of 26.86(26.82) mA/cm(2), and a fill factor of 70.6(70.0)% when measured under forward (reverse) voltage scan. The average PCE of 50 cells we have fabricated is 14.39 +/- 0.33%, indicating good reproducibility.