Co/N-HNTs composites were synthesized via a one-pot solvothermal method, where amine functional halloysite nanotubes (N-HNTs) were used as support materials. Effects of sulfosuccinate sodium salt (AOT), an anionic surfactant, on morphology and dispersibility of Co particles anchored at the N-HNTs were studied. The dispersibility of the Co particles was promoted with the increase of the AOT concentration. The as-obtained composite was used as a catalyst to generate H-2 gas by hydrolysis of NaBH4 solution. The catalytic activity of the composite was significantly enhanced than the pure Co and Co/graphene composite at the same experimental conditions reported by our laboratory, and the catalyst was conveniently separated from the solution by a magnet. The catalytic activity was enhanced when the dispersibility of the Co particles was improved at the surface of the N-HNTs and the Co content contained in the composite was lowed. At the same time, the Co particles anchored at the inner surface of the N-HNTs resulted in higher catalytic activity, where the Co particles may bond with nitrogen atoms. The activation energy for the hydrolysis of NaBH4 was calculated to be about 15.42 kJ mol(-1). The catalyst can be continuously used for four times with about the same catalytic activity. (C) 2016 Elsevier B.V. All rights reserved.