High-performance thin film composite (TFC) forward osmosis (FO) membranes with a low degree of internal concentration polarization (ICP) are critical for concentrating high-salinity wastewaters. This report focuses on the preparation of TFC FO membranes via a sacrificial approach. In order to improve the FO flux, hydrophilicity and morphology of the support membrane were mainly investigated. The hydrophilicity of the polysulfone (PSF) substrate was tuned by blending with sulfonated poly (ether ether ketone) (SPEEK), and the resulting SPEEK blended PSF membrane was denoted as SPSF substrate. The pore structure of the SPSF membrane was tailored by the application of a co-casting technique, which yielded a TFC membrane with a structure parameter (S) of 191 mu m. In contrast, the TFC membranes based on the PSF and SPSF substrates through single layer casting showed S values of 527 mu m and 361 mu m, respectively. These results indicate that the combined hydrophilicity and open pore structure are responsible for the lowered S value. Further application of the hydrophilic substrate based TFC membranes in the treatment of high salinity wastewaters (10 wt%) demonstrated the higher initial water flux (283 L/m(2.)h) with a water recovery rate of 532% in comparison to the TFC membrane based on the pristine PSF through the single layer casting. This new method paves a way to generate high-performing FO membranes. (C) 2016 Elsevier B.V. All rights reserved.