The use of biomass templating materials with a cheap production method as an enhanced sorbent for CO2 uptake has been proposed recently. However, the attrition and fragmentation behaviour of this type of material, which is a vital parameter for calcium looping sorbents, has not yet been investigated in detail. In this work the fragmentation behaviour of biomass-templated sorbents is investigated. Three types of materials were prepared using a mechanical pelletiser: 1. lime and cement (LC); 2. lime and flour (LF); and 3. lime, cement and flour (LCF). These samples were heat treated in a pressurised heated strip reactor (PHSR) and in a bubbling fluidised bed (BFB) and changes in particle size distribution were measured to assess fragmentation. Results indicated that the addition of biomass enhances the propensity to undergo fragmentation. Upon heat treatment in the PHSR the particle size of LC was not modified significantly; on the contrary the mean particle diameter of LF decreased from 520 mu m to 116 mu m and that of LCF from 524 mu m to 290 mu m. Fragmentation tests in the BFB confirmed the trend: 67% of the particles of LF fragmented, against 53% of LCF and 18% of LC samples. The addition of cement to the LF samples partially counteracts this performance degradation with respect to attrition. However, calcium aluminate pellets (LC) showed the lowest rate of fragmentation amongst all of the samples tested. (C) 2016 Published by Elsevier Ltd.