LiMn2-xGdxO4 (x = 0.00, 0.01 and x = 0.04) spinel active material were prepared by sol-gel method. The morphology, crystal structure, thermal stability and electrochemical properties of the synthesized samples were evaluated. Gd-doping maintains the cubic spinel structure of LiMn2O4, leads to a decrease of the average particle size, and has a strong influence on the electrochemical properties of the cathodes. LiMn(2-x)G(x)O(4) cathode materials show two pairs of separated redox peaks, independently of the Gd-doping. After 40 charge-discharge cycles at C/2, the discharge capacity was 55.9 mAh.g(-1) and 33 mAh.g(-1) for x = 0.04 and x = 0, respectively, corresponding to a capacity retention of 80% and 70%, respectively. The Gd-doped with x = 0.04 showed improved cycling performance with respect to pristine LiMn2O4 due the smaller particle size and superior structural stability, showing its suitability for lithium-ion battery applications. (C) 2016 Elsevier B.V. All rights reserved.