A novel solid-to-solid phase change composite brick was prepared by combination of polyurethane (PU) and pitch-based graphite foam (PGF). The carbonaceous support, which can be used for mass production, not only greatly improves the thermal conductivity but promote electro-to-heat conversion efficiency of organic phase change materials (PCMs). Our composite retained the enthalpy of PCM and exhibited a greatly reduced supercooling temperature. The novel composite was investigated by differential scanning calorimetry (DSC), thermogravimetric analysis (TGA) and scanning electron microscope (SEM). The enthalpy of polyurethane has increased about 8.6% after infiltrating into graphite foam. The composite was very stable during thermal cycle test, and the electro-to-heat conversion efficiency achieves to 85% at lower voltages (1.5-1.8 V), which can vastly reduce energy consumption. The as-prepared composite was used in a wear layer to test its performance comparing with normal fabric. (C) 2016 Elsevier Ltd. All rights reserved.