Herein, a series of microcapsules, containing n-hexadecane (HD) as the core, and polymethyl methacrylate (PMMA) and poly(butyl acrylate-co-methyl methacrylate) (poly(BA-co-MMA)) as the shells were prepared through suspension polymerization. The aim of this work was to investigate the effect of shell flexibility on the encapsulation efficiency and thermal performance of the microcapsules. Kinetics and thermodynamic studies based on propagation rate constants for the monomers and the polarity of the system were employed to predict final morphology of the microcapsules. To this aim, contact angle and interfacial tension analysis were performed, and the results of morphology prediction were affirmed by SEM. A multi-nucleus morphology was observed for microcapsules with PMMA shell and a matrix type morphology was detected for poly(BA-co-MMA) with high BA content. Thermal properties of the microcapsules were evaluated by DSC and DMTA was performed to assess the rigidity of shells with two distinct Tgs for poly(BA-co-MMA). Appropriate thermal storage behavior plus flexibility of the shell in PCM microcapsules must be considered simultaneously for efficient applications. Here, poly(BA-coMMA) (with BA content below 25 wt%) as the shell was nominated for this reason. (C) 2017 Elsevier Ltd. All rights reserved.