This research aimed to investigate the photoelectrochemical response and corrosion behavior of CdS/TiO2 nanocomposite films using electrochemical measurements in an aerated 0.5 M NaCI solution under white light illumination. The CdS/TiO2 nanocomposite films were prepared by chemical bath deposition technique in a solution of cadmium and sulfide ions. The high resolution images of CdS/TiO2 nanocomposite films were provided by field emission scanning electron microscope. Theirs chemical identification and quantitative compositional information, crystallinity and actual chemical compounds formed were determined by energy dispersive spectroscopy, X-ray diffraction and X-ray photoelectron spectroscopy, respectively. The results indicated that the photoelectrochemical activity of the films depended strongly on CdS content. From the preparation of CdS/TiO2 nanocomposite films by 5,10 and 15 dipping cycles in the chemical solutions, the best photoelectrochemical response was revealed by the 10 dipping cycles prepared film. Galvanic couple testing demonstrated that the photoelectrochemical response of the film decreased continuously compared to that of anodized nanoporous TiO2 substrate which described by photocorrosion of CdS nanoparticles. In addition, chloride-ion attack also induced pitting corrosion leading to fluctuation and deterioration of photoelectrochemical response. CdO2 and Cd(OH)(2) depositions were found as the main photocorrosion products on collapsed nanostructured-surface. The relevance between photoelectrochemical response and corrosion behavior of CdS/TiO2 nanocomposite film was discussed in detail. (C) 2017 Elsevier B.V. All rights reserved.