Six different types of Au nanostructures with rough surfaces were readily prepared through the redox reactions between Au precursor, AuCl4-, and furfuryl derivatives without extra metal surface capping ligands, in deionized water at room temperature. Furfuryl alcohol (FA) or furfurylamine (FFA) was used as a sole reducing agent for the reduction of Au precursor. Both FA and FFA effectively polymerized during the redox reactions to form polyfuran polymers. These polymers are thought to act as surface capping ligands during the formation of Au nanostructures. Experiments were conducted with three different concentrations of each furfuryl derivative. Interestingly, Au particles prepared from the reaction with varying concentration of FA or FFA showed large differences in size, and revealed that the higher the ratios of [FA]/[AuCl4-] or [FFA]/[AuCl4-], the smaller the size of Au particles. The size of Au particles was in the range of 1 mu m to under 30 nm. Among these samples, two nanostructured Au particles, AuFA-4 and AuFFA-1, deposited on a Si wafer by a simple drop-casting method, were revealed as highly active surface enhanced Raman scattering (SERS) substrates for the detection of methylene blue (MB) and crystal violet (CV). High SERS enhancement factors (EFs) of 10(6) similar to 10(8) for MB and CV were observed. Small size Au nanoparticles (AuFFA-2 and AuFFA-4) were also found to be very active for the catalytic hydrogenation of 4-nitrophenol to 4-aminophenol in the presence of NaBH4 at room temperature. AuFFA-2 could be recycled eight times, without losing its activity. (C) 2017 Elsevier B.V. All rights reserved.