The microstructural evolution, orientation relationships, boundary characteristics, grain type, local deformation, and microhardness across the welded interface of duplex stainless steel (DSS) were investigated. The DSS welded joint consisted of four typical zones: base metal (BM), low-temperature heat-affected zone (LTHAZ), high-temperature heat-affected zone (HTHAZ), and weld metal (WM). The apparent microstructural changes in the HTHAZ and LTHAZ were secondary austenite and Cr2N precipitation. A modified cooperative precipitation mechanism of secondary austenite and Cr2N at the interface was proposed. Furthermore, the ferrite in both the HTHAZ and LTHAZ maintained the same distribution as the ferrite texture in the BM, while this ferrite texture disappeared completely in the WM. Different austenite grains in the different zones exhibited different orientation relationships with the ferrite matrix. Special grain boundaries were mainly distributed between the austenite grains, while the ferrite grains primarily contained random grain boundaries. Austenite twins constituted the largest proportion of the special boundaries. The special austenite grain boundaries in the BM and LTHAZ were higher in relative frequency than those in the HTHAZ and WM. The ferrite grains in the HTHAZ and WM mainly consisted of substructured grains. In the BM, the recrystallization degree of ferrite was significantly lower than that of austenite grains. The local deformations were mainly generated in the grain boundaries and within the deformed grains. The HTHAZ exhibited the highest hardness, while the BM had the lowest hardness. The LTHAZ had a lower hardness than the HTHAZ and higher hardness than the BM. (C) 2017 Elsevier B.V. All rights reserved.