Deciphering the structural and volume changes occurring during electrode reactions in lithium-ion batteries is perhaps a boon for high energy density batteries. Here, we report the synthesis of 3D network of dichalcogenide molybdenum disulfide (MoS2) encapsulated over nitrogen rich graphitic carbon nitride nanosphere (g-C3N4) forming an interconnected and uniform g-C3N4/MoS2 scaffolds. The crystallinity, phase purity, morphological features and elemental composition were evaluated through XRD, FESEM, TEM, HRTEM, BET and XPS analyses. The electrochemical properties of N-rich g-C3N4/MoS2 scaffolds were investigated as potential anode materials for lithium-ion batteries. Electrochemical testing of the g-C3N4/MoS2 constructured electrode delivered reversible capacity of 857 mAh g(-1) at 0.1 C rate after fifty cycles and exhibited a high rate performance with reversible capacity of 383 mAh g(-1) at 10 C rate (higher than theoretical capacity of graphite, 372 mAh g(-1)). The superior electrochemical property of gC(3)N(4)/MoS2 is attributed to N-rich carbon support which favors better electronic conductivity, and affords more sites for Li+ ions. The nitrogen rich carbon nitride accommodates volume changes caused during repeated charge/discharges and maintains high structural integrity and specific capacity. (C) 2017 Elsevier B.V. All rights reserved.