Bioelectrochemical systems (BESs) employ extracellular electron transfer from bacteria that grow at electrodes. Due to biofilm and electrode limitations, industrial-scale applications require large electrode areas, and thus inexpensive electrode materials. Here, electro-spun polyacrylonitrile (PAN) and carbon nanofiber (CNF) were manufactured. In addition, the conductive polymer poly(3,4-ethylenedioxythiophene) (PEDOT) was applied as a coating to these materials and to carbon cloth (CC). We tested these materials as electrodes by using physicochemical measurements, cyclic voltammetry, and bioelectrochemical growth-studies with Geobacter sulfurreducens. PAN is a nonconductive material without capacitance, but with PEDOT coating the conductivity and capacitance became sufficient to support electric current production in our BES. CNF outperformed CC in capacitance, but behaved similarly in our BES when normalized to projected surface area. With the PEDOT coating, CNF increased electric current production by 38% in our BES, while this was 64% for CC. When applied to a gold microfluidic electrode, electric current with G. sulfurreducens increased almost three-fold. PEDOT added considerable specific surface area to electrodes possessing a low surface area, but not with a high surface area such as CNF. This work demonstrates that electro-spun electrodes and PEDOT coating are a promising electrode alternative that can be readily implemented into existing BESs. (C) 2017 Elsevier B.V. All rights reserved.