The synthesis of microporous polymers generally requires postpolymerization modification via hyper cross-linking to trap the polymeric network in a state with high void volume. An alternative approach utilizes rigid, sterically demanding monomers to inhibit efficient packing, thus leading to a high degree of free volume between polymer side groups and main chains. Herein we combine polymers of intrinsic microporosity with polymerization-induced microphase separation (PIMS), a versatile methodology for the synthesis of nanostructured materials that can be rendered mesoporous. Copolymerization of various styrenic monomers with divinylbenzene in the presence of a poly(lactide) terminated with a chain-transfer agent (PLA-CTA) results in kinetic trapping of a microphaseseparated state. Subsequent etching of PLA provides a bicontinuous mesoporous network. Using equilibrium and kinetic nitrogen sorption experiments as well as positron annihilation lifetime spectroscopy (PALS), we demonstrate that variations in the steric characteristics of the styrenic monomer impart the network with microporosity, resulting in hierarchically (meso and micro) porous materials. Additionally, structure property relationships of the styrenic monomer with total surface area and pore volume indicate that the glass transition temperature (Tg) of the corresponding styrenic homopolymers provides a reasonable measure of the steric interactions and resultant microporosity in these systems. Finally, PALS provides insight into micro- and mesoscopic void volume differences between porous monoliths containing either tent butyl or TMS-modified styrenic monomers compared to the parent, unmodified styrene.