Silicon porosification by silver assisted chemical etching (Ag-ACE) for a short range of H2O2 concentration is reported. We experimentally show that porous silicon (PSi) is obtained for 1% H2O2, whereas silicon nanowires (SiNWs) appeared by simply tuning the concentration of H2O2 to relatively high concentrations up to 8%. The morphological aspects are claimed by scanning electron microscopy proving that the kinetics of SiNWs formation display nonlinear relationships versus H2O2 concentration and etching time. A semiqualitative electrochemical etching model based on local anodic, Ic, and cathodic, Ia, currents is proposed to explain the different morphological changes, and to unveil the formation pathways of both PS and SiNWs. More importantly, an efficient antireflective character for silicon solar cell (reflectance close to 2%) is realized at 8% H2O2. In addition, the luminescence of the prepared Si-nanostructures is claimed by photoluminescence which exhibit a large enhancement of the intensity and a blue shift for narrow and deep SiNWs. (C) 2017 Elsevier B.V. All rights reserved.