In order to improve the dry sliding tribology properties of mild steel compound, the in-situ WC carbide coatings with 18, 32, 54 vol% WC were successfully synthesized using plasma transferred arc metallurgic reaction (PTAMR) with alloy powders W,C and Fe-30Ni. The composition, microstructure and microhardness of the carbide coatings were characterized. It was found that the carbide coating consisted of WC, M6C and gamma phases, carbides distribute gradually from the coating bottom to top, the in-situ WC crystal grows into triangle prism structure with high hardness and good toughness. Dry sliding tribology behaviors were studied on block-on-wheel dry sliding wear tester with load 300 N, sliding speed 0.836 m/s and distance 500 m. Results show that the friction coefficient diagrams contain three stages, variation of friction coefficient increase with the content of WC, friction temperature increase with the sliding distance, increasing the content of WC can directly increase the antiwear property of WC/Fe carbide coating. The main wear mechanisms of in-situ WC/Fe carbide coating are adhesive, oxidation, micro-cutting and ploughing wear. (C) 2017 Elsevier B.V. All rights reserved.