Graphene oxide (GO) was first employed as a support in preparing TiO2 nanoparticles by adsorbed-layer nanoreactor synthesis (ALNS). Both TiO2 crystallization and GO reduction simultaneously occurred during solvothermal treatment with alcohol as a solvent. By transmission electron microscopy, high resolution transmission electron microscopy, X-ray diffraction, X-ray photoelectron spectroscopy, Fourier transform infrared spectroscopy, and photoluminescence spectroscopy, the results showed that TiO2 nanoparticles with less than 10 nm of size distributed very homogeneously on the GO surface. Tight interaction between TiO2 particles and GO surface could effectively inhibit the aggregation of TiO2 particles, during solvothermal treatment for anatase TiO2 formation. Alcohol could also reduce oxygenated functional groups on GO surface after solvothermal treatment. TiO2 particles with small size and the decrease in oxygenated functional groups on the GO surface both caused high separation efficiency of photo-generated charge carriers, thus resulting in high photo-degradation performance of catalysts. Strong phenol adsorption on photocatalyst was key to enhancing photo-degradation efficiency for phenol in seawater. Moreover, the change in catalyst structure was minimal at different temperatures of solvothermal treatment. But, the degradation rate and efficiency for phenol in seawater were obviously enhanced because of the sensitive structure-activity relationship of catalysts under weak-light irradiation. (C) 2017 Elsevier B.V. All rights reserved.