Average self-diffusion coefficients of hydrated protons in sulfonated poly (ether sulfone) (SPES), Interpolymer and Nafion 117 membranes are measured by impedance spectroscopy and pulsed field gradient nuclear magnetic resonance (PFG NMR). Self-diffusion coefficient measured by impedance spectroscopy shows two patterns, one is at the low hydration states, i.e. lambda = 2-4 and another at the high hydration states (starting from lambda = 4). At lower hydration states the diffusion values increases slowly while steep increment is found at higher hydration level. PFG NMR shows similar trend throughout the measurements. The diffusion coefficients at higher temperatures are higher than at lower temperatures as a function of lambda for SPES membrane. At the same value of lambda, hydrated proton self-diffusion coefficient is found to be increased by 18% from 295.5 to 303 K. The thermo-mechanical properties of the membranes characterised by the means of DSC, TGA and DMA analysis show SPES, stable up to 450 degrees C and can be used for the high-temperature applications.