Spinel FeCo2S4 nanoflower arrays grown on Ni foam (FeCo2S4@Ni) have been successfully fabricated via a facile hydrothermal sulfurization of the corresponding FeCo2O4 precursor. The results of X-ray diffraction and X-ray photoelectron spectroscopy characterizations affirm that partial Co2+/Co3+ ions in Co3S4 have been substituted by Fe2+/Fe3+ ions to form FeCo2S4. The obtained FeCo2S4@Ni exhibits an ultrahigh specific capacitance (1644.07 mF cm(-2) at 50 mA cm(-2)) and a supreme cycling stability (similar to 100% after 10,000 cycles at 50 mA cm(-2)) as binder-free electrodes for supercapacitors. The cycling stability of the fabricated product is the highest among the documented ternary metallic sulfides so far. The excellent supercapacitive performance of FeCo2S4@Ni emanates from the unique architectures of Fe2Co2S4 nanoflower arrays constituted by ultrathin nanoflakes, three-dimensional porous and conductive Ni foam, and solid skeleton of Ni foam for robust connections to the Fe2Co2S4. (C) 2017 Elsevier B.V. All rights reserved.