InAs/GaSb nanoridge heterostructures were grown on V-grooved (0 0 1) Si by metal organic chemical vapor deposition. Combining the aspect ratio trapping process and a low temperature GaAs buffer, we demonstrated high quality GaSb nanoridge templates for InAs/GaSb heterostructure growth. Two different interfaces, a transitional GaAsSb and an InSb-like interface, were investigated when growing these heterostructures. A 500 degrees C growth temperature in conjunction with a GaAsSb interface was determined to produce the optimal interface, properly compensating for the tensile strain accumulated when growing InAs on GaSb. Without the need for a complicated switching sequence, this GaAsSb-like interface utilized at the optimized temperature is the initial step towards InAs/GaSb type II superlattice and other device structures integrated onto Si. (C) 2017 Elsevier B.V. All rights reserved.