Gallium phosphide (GaP) nanowire film electrodes have been prepared via solid sublimation of GaP powder using both gold (Au) and tin (Sn) nanoparticles as the vapor-liquid-solid (VLS) catalysts on Si(1 1 1) and GaP(1 1 1)B substrates. The resultant GaP nanowires are compared and contrasted in terms of structures and photoactivity in photoelectrochemical half cells. Raman spectra implicated a difference in the surface condition of the two types of nanowires. Complete wet etching removal of metallic VLS catalysts from the as-prepared GaP nanowires was possible with Sn catalysts but not with Au catalysts. The photoresponses of both Sn- and Au-seeded GaP nanowire films were collected and examined under 100 mW cm(-2) white light illumination. Au-seeded nanowire films exhibited strong n-type characteristics when measured in nonaqueous electrolyte with ferrocene/ferricenium as the redox species while Sn-seeded nanowires showed behavior consistent with degenerate n-type doping. (C) 2017 Elsevier B.V. All rights reserved.