In order to reduce the leaching of pollutants and remove the Al and Zn/Al alloy from municipal solid waste incineration bottom ash (MSWIBA), an optimized alkaline pre-treatment procedure was developed in this study. The influences of alkaline conditions on the removal rate of Al and Zn/AI alloy were investigated, including [OH](-) concentration, temperature, particle size, liquid/solid ratio and treatment duration. The experimental results showed that the optimized alkaline pre-treatment conditions to efficiently remove the Al and Zn/Al alloy was by using a minimum of 1.0 mol/l [OH](-), at 55 degrees C and with a minimal liquid/solid ratio of 5. The removal rate of Al and Zn/Al alloy followed an S-shape curve, in which the slow beginning stage was attributed to the protection of the oxidation layer and the quenched product around the Al and Al/Zn alloy. After 3 h of the optimized alkaline pre-treatment, the leaching of Cr, Cu, Pb and Zn of the treated MSWIBA was reduced by more than 90% of that of the original MSWIBA. The alkali-silica reaction test further indicated that the expansion of concrete prepared with the pre-treated MSWIBA was significantly reduced and there was no macro-crack or spalling damage on the surface of the tested specimens. (C) 2017 Elsevier B.V. All rights reserved.