Composites based on expanded graphite (EG) and metal oxides (MOs) were prepared by an explosive combustion and blending method. A metal oxide (Ag2O, CuO or ZnO)-containing phase was employed as a component with reactive functionality, which was supported on EG as a component with adsorptive functionality. The physical properties of the EG/MO composites were examined using SEM and FTIR spectroscopy, the results of which indicated that the MOs were incorporated in the EG matrix after impregnation. Solid state magic angle spinning (MAS) H-1, P-31 and cross polarization (CP) MAS C-13 NMR studies of the EG/MO composites were performed after adsorption of dimethyl methylphosphonate (DMMP). The FTIR and NMR data showed that the initial uptake occurred through both molecular and reactive adsorption. Molecular adsorption occurred by van der Waals interaction of M(Zn, Cu, Ag) center dot center dot center dot O=P and hydrogen-bond formation to isolated hydroxyl groups. Reactive chemisorption appeared to occur through interaction with both Lewis acid sites and active oxygen species present on the MO surface. The FTIR and NMR results exhibited a trend of reactivity towards DMMP in the order Ag2O > ZnO > Cu O, which indicated stronger interaction between the Lewis acid sites and the phosphoryl O atom of DMMP for Ag2O as compared with ZnO and CuO, with concomitant formation of surface-coordinated DMMP and bridge-bonded OAPAO phosphorus oxide species. (C) 2018 Elsevier B.V. All rights reserved.