By the way of hydrothermal reaction, the MoS2 nanoparticles were loaded on the surface of GO sheets uniformly. Then, the MoS2-RGO composites were modified with gamma-(2,3-epoxypropoxy) propytrimethoxysi lane (KH560), and followed by preparing the MoS2-RGO/epoxy composite coatings. The morphology and structure of MoS2-RGO were characterized though SEM, TEM, FT-IR and XPS. Besides, the corrosion resistance properties of the as-prepared MoS2-RGO/epoxy composite coatings were characterized by means of electrochemical impedance spectroscopy (EIS) and polarization curves analysis, and then the thermal stability and water permeability resistance of coatings were characterized. The results showed that the MoS2 could be loaded on the surface of GO uniformly when the ratio between MoS2 and GO is 1:1. The anti-corrosion property and permeability resistance of the MoS2-RGO/epoxy composites coating was enhanced significantly due to its excellent barrier property. Besides, the thermal property analysis exhibits that the lamellar structure of MoS2, GO and MoS2-RGO can effectively block the escape of the pyrolysis products, resulting in the maximum thermal weightlessness reduced. (C) 2018 Elsevier B.V. All rights reserved.