Photoelectrochemical (PEC) performances of the anatase TiO2 films hydrothermally grown on the seeded fluorine-doped tin oxide (FTO) substrates are examined in this work. Structural characterizations of the TiO2 films were conducted using Raman scattering spectroscopy. Although there is no obvious rutile peak appearing, an asymmetrical peak centered at similar to 399 cm(-1) was observed in the Raman spectra of the TiO2 films deposited either on the low-temperature-formed seed layers or with low concentrations of Ti precursor. The asymmetrical Raman shift can be deconvoluted into the B-1g mode of anatase and E-g mode of rutile TiO2 peaks centered at similar to 399 cm(-1) and similar to 447 cm(-1), respectively. Therefore, a minute quantity of rutile phase was inspected in the anatase film using Raman scattering spectroscopy. With the same light harvesting ability, we found that the PEC performance of the anatase TiO2 film was significantly enhanced as the minute quantity of rutile phase existing in the film. It is ascribed to the formation of the anatase/rutile heterojunction which is beneficial to the charge separation in the photoanode. (C) 2018 Elsevier B.V. All rights reserved.