A commercial Fe-C material (P265GH) used for natural gas delivery and transportation systems was analyzed in H2S atmosphere in order to establish the corrosion resistance. In most of the industrial processes for gas purification the corrosion rate is speed up by the presence of sulphur (S) especially as ions (HS-, SO32-) or different species like H2S. The H2S (hydrogen sulphide) is, beside a very toxic compound, a very active element in the acceleration of metallic materials deterioration. For experiments we used a three electrodes cell with Na2SO4 + Na2S solution at pH 3 for two different temperatures, room temperature similar to 25 degrees C (sample 1) and at 60 (sample 2) +/- 1 degrees C in order to realize EIS (electrochemical impedance spectroscopy) and potentiodynamic polarization. After electro-chemical tests and corrosion resistance characterisation the material surface was analyzed using scanning electron microscopy (SEM), X-ray diffraction (XRD) and energy dispersive spectroscopy (EDS). (C) 2017 Elsevier B.V. All rights reserved.