Herein, we demonstrated the simultaneous formation of multi-component heterojunction consisting graphitic carbon nitride (g-C3N4) and C, N co-doped anatase/rutile mixed phase by using facile sol-gel assisted heat treatment. The evolution of core-shell nanostructures heterojunction formation was elucidated by varying the temperature of heat treatment from 300 degrees C to 600 degrees C. Homogeneous heterojunction formation between g-C3N4 and anatase/rutile mixed phase was observed in gT400 with C and N doping into TiO2 lattice by O substitution. The core-shell nanoarchitectures between g-C3N4 as shell, and anatase/rutile mixed phase as core with C and N atoms are doped at the interstitial positions of TiO2 lattice was observed in gT500. The result indicated that core-shell nanoarchitectures photocatalyst (gT500) prepared at 500 degrees C exhibited the highest photocatalytic activity in the degradation of methyl orange under visible light irradiation. Meanwhile, the possible mechanisms of charge generation, migration, action species and reaction that probably occur at the gT500 sample were also proposed. The photodegradation results of gT500 correlated completely with the results of the PEC and photoluminescence analysis, which directly evidenced improved charge separation and migration as the crucial parameters governing photocatalysis. It is worthy to note that, the simultaneous formation of multicomponent heterojunction with core-shell structure provided an enormous impact in designing highly active photocatalyst with superior interfacial charge transfer. (C) 2017 Elsevier B.V. All rights reserved.