The membrane carbon materials with hierarchical porous architecture are attractive because they can provide more channels for ion transport and shorten the ions transport path. Herein, we develop a facile way based on "confined nanospace deposition" to fabricate N-dopi-ng three dimensional hierarchical porous membrane carbon material (N-THPMC) via coating the nickel nitrate, silicate oligomers and triblock copolymer P123 on the branches of commercial polyamide membrane (PAM). During high temperature treatment, the mesoporous silica layer and Ni species serve as a "confined nanospace" and catalyst respectively, which are indispensable elements for formation of carbon framework, and the gas-phase carbon precursors which derive from the decomposition of PAM are deposited into the "confined nanospace" forming carbon framework. The N-THPMC with hierarchical macro/meso/microporous structure, N-doping (2.9%) and large specific surface area (994m(2) g(-1)) well inherits the membrane morphology and hierarchical porous structure of PAM. The N-THPMC as electrode without binder exhibits a specific capacitance of 252 F g(-1) at the current density of 1 A g(-1) in 6 M KOH electrolyte and excellent cycling stability of 92.7% even after 5000 cycles. (c) 2017 Elsevier B.V. All rights reserved.