Graphene reinforced Al composite with high mechanical property was successfully reported. However, there are quite limited studies about shot peening effect on this new type material. Here, 1.0 wt% graphene reinforced Al composite was produced by powder metallurgy and treated by shot peening. The surface layer characteristics of shot peened composite was investigated by X-ray diffraction line profile analysis. The microstructure including domain size, micro-strain, dislocation density and crystalline texture were analyzed. The results showed that after surface shot-peening, the domain size were refined, the dislocation density of the composite was increased sharply to 9.0 x 10(11)/cm(2) at the top surface. The original strong texture was diminished after shot peening. Based on the calculated results, the microstructure variation of composite was more severe than that of Al without graphene reinforcement after shot peening. Besides, the micro-hardness of composite at the top surface increased up to 75HV one time higher than that of matrix. It is concluded that shot peening can be considered as an essential process of improving the surface properties of graphene reinforced Al composite. (C) 2017 Elsevier B.V. All rights reserved.