Efficient electrocatalytic water splitting is one of the most effective ways to solve the global energy crisis. In this paper, we report on a novel self-assembled hierarchical structure of Co3O4/CoMoO4 grown in situ on a bare nickel foam. The unique, three-dimensional honeycomb-like Co3O4 pores were constructed from one-dimensional nanowires and coated on two-dimensional CoMoO4 nanosheets structures grown on nickel foam. The synthesis involved a step-wise solvothermal method followed by an annealing treatment. Benefiting from the synergistic effect of the hierarchical nanostructures, the materials had more reaction active sites and a smaller electron transfer impedance, and they exhibited excellent electrocatalytic performances for the HER and OER of 143 and 244 mV, respectively, at 10 mA cm(-2) in an alkaline solution. Furthermore, the materials remained stable during the long electrolysis period, over 10 h, presenting promising application prospects in the field of electrocatalytic water splitting. (C) 2017 Published by Elsevier B.V.