Atomic force microscopy (AFM) was used to characterize the attractive force, adhesive force and adhesion energy between an AFM probe tip and nanometric soot particle generated by a premixed methane/oxygen flame. Different attractive force distributions were found when increasing the height above burner (HAB), with forces ranging from 1.1-3.5 nN. As the HAB was increased, the average attractive force initially increased, briefly decreased, and then underwent a gradual increase, with a maximum of 2.54 nN observed at HAB = 25 mm. The mean adhesive force was 6.5-7.5 times greater than the mean attractive force at the same HAB, and values were in the range of 13.5-24.5 nN. The adhesion energy was in the range of 2.0-5.6 x 10(-17)J. The variations observed in the average adhesion energy with increasing HAB were different from those of the average adhesion force, implying that the stretched length of soot particles is an important factor affecting the average adhesion energy. The Hamaker constants of the soot particles generated at different HABs were determined from AFM force-separation curves. The average Hamaker constant exhibited a clear correlation with the graphitization degree of soot particles as obtained from Raman spectroscopy. (C) 2017 Elsevier B.V. All rights reserved.