Corncob was torrefied under nitrogen and carbon dioxide atmospheres at 220-300 degrees C, obtaining solid products with mass yields of 69.38-95.03% and 67.20-94.99% and higher heating values of 16.58-24.77 MJ/kg and 16.68-24.10 MJ/kg, respectively. The changes of physicochemical properties of the charcoal was evaluated by many spectroscopies, contact angle determination, and combustion test. Hemicelluloses were not detected for the torrefaction under the hard conditions. As the severity increased, C concentration raised while H and O concentrations reduced. Combustion test showed that the burnout temperature of charcoal declined with the elevation of reaction temperature, and torrefaction at a high temperature shortened the time for the whole combustion process. Base on the data, torrefaction at 260 degrees C under carbon dioxide was recommended for the torrefaction of corncob.