Amorphous and crystalline copper cobalt sulfides are successfully synthesized via a hydrothermal method at different temperatures and researched as electrode materials for supercapacitor. The reaction mechanisms during the sulfidation and hydrothermal processes are investigated and clarified. It is demonstrated that the hydrothermal temperature is a crucial factor for the crystallinity, morphology and electrochemical performance of CuCo2S4. Among all the samples, the CuCo2S4 synthesized at 150 degrees C shows the highest specific capacitance of 515 F g(-1) at 1 A g(-1) as well as good cycling stability with similar to 93.3% capacitance retention after 10000 cycles at 5 A g(-1). An asymmetric device which is assembled by using optimized CuCo2S4 electrode as positive electrode and activated carbon as negative electrode material is able to deliver an ultrahigh energy density of 50.56 Wh kg(-1) at a power density of 4.6 kW kg(-1), and remains 20.93 Wh kg(-1) at a high power density of 22.5 kW kg(-1), with similar to 99% capacity retention after 10000 cycles. Based on the results above, the CuCo2S4 materials prepared by our method possess a considerable potential as electrode materials for supercapacitor applications. (C) 2018 Elsevier Ltd. All rights reserved.