Layered transition metal oxides are considered to be promising candidates as cathode materials for sodium-ion batteries. Herein, a facile solid-state reaction is developed to synthesize hexagons plate-like Na0.67Ni0.25Mn0.75O2 (+) (delta) (denoted as P2-NNM) material with habit plane formed. The structure of this layered oxide is characterized by XRD, HR-TEM and SAED. The layered material delivers a high reversible capacity of 91.8 mAh g(-1) at 0.2 C with a capacity retention of 94.4 % after 280 cycles, superior rate capability and long cycle life (84.2 % capacity retention after 1000 cycle). Ni2+ is an active ion and Ni doping alleviates the Jahn Teller distortion, and Mn3+/Mn4+ coexist as Mn4+ is desired from the stability perspective. Particularly, CV and XPS results confirm these results. Moreover, the electrode exhibits a quasi-solid-solution reaction during the sodium extraction and insertion. This contribution demonstrates that P2-NNM is a promising cathode electrode for rechargeable long-life sodium-ion batteries.