This paper studies the effects of propylene, methyl methacrylate (MMA) and isopropanol (IPA) in air on the spatial performance of proton exchange membrane fuel cells (PEMFCs). The introduction of 100 ppm C3H6 into the oxidant stream resulted in a performance decrease of 130 mV at 1.0 A cm(-2), whereas 20 ppm MMA caused a voltage loss of 80 mV. A moderate performance decline of 60 mV was detected in the presence of 5.3.10(3) ppm IPA in air. Spatial electrochemical impedance spectroscopy (EIS) data showed an increase in charge and mass transfer resistances under exposure to C3H6 and MMA, although IPA did not affect the impedance. The observed PEMFC performances, local current redistributions and EIS data can be explained by the adsorption of contaminants on the Pt surface, their subsequent transformations, and their impacts on the electrochemical surface area and oxygen reduction mechanism. It was assumed that the studied contaminants were oxidized mainly to CO2 via electrochemical and chemical pathways under the operating conditions and at the cathode potential. Self-recovery of PEMFC performance was observed for each contaminant after halting its introduction into the air. Possible contaminant oxidation/reduction mechanisms and their correlations with spatial performance and EIS are presented and discussed.