Polyacrylic acid (PAA) was grafted onto the surface of silicone rubber membrane (SR) by plasma-induced graft copolymerization (PIP). Ar-plasma was used to activate the surface of SR. Also, a determination was made of the influences of plasma treatment power, pressure, time, grafted copolymerization reaction time, and monomer concentration on polymerization yield. The surface properties of SR were measured by ATR-FTIR, ESCA, and SIMS. In those analyses, the elemental composition and different carbon bindings on the surface of SR were examined by ESCA with the amount of O1s/C1s being approximately 0.7 at 60 s by Ar-plasma treatment (60 W, 200 mtorr). The peroxide group introduced on SR was measured via 1,1-diphenyl-2-picryhydrazyl (DPPH). The optimum amount of peroxide groups was 6.85 x 10(-8) mol/cm(2) at 60 s of Ar-plasma treatment. The peroxide group (33D peak) was introduced onto the surface of SR by negative spectra of SIMS analysis after SR treatment by Ar-plasma. An increase was obtained in grafted polymerization yield with a region of 5 to 50% (v/v) of acrylic acid aqueous solution. Both sites of polyacrylic acid were detected after staining by toluidine blue O. That is, a homobifunctional membrane was developed via this surface modification method.