A study of heat capacity, thermal dilatation, susceptibility to hydrostatic pressure, permittivity and polarization loops was carried out on NH4HSO4-porous glass nanocomposites (AHS + PG) as well as empty glass matrices. The formation of dendrite clusters of AHS with a size, d (cryst), exceeding the pore size was found. An insignificant anisotropy of thermal expansion of AHS + PG showing statistically uniform distribution of AHS with random orientations of nanocrystallites over the matrix was observed. The effect of internal and external pressures on thermal properties and permittivity was studied. At the phase transition P-1 a dagger" Pc, a strongly nonlinear decrease in the entropy Delta S (2) and volume strain (Delta V/V) (T2) was observed with decreasing d (cryst). The linear change in temperatures of both phase transitions P-1 a dagger" Pc a dagger" P2(1)/c under hydrostatic pressure is accompanied by the expansion of the temperature range of existence of the ferroelectric phase Pc, while this interval narrows as d (cryst) decreases.