Journal of Power Sources, Vol.388, 25-31, 2018
Dense garnet-like Li5La3Nb2O12 solid electrolyte prepared by self consolidation method
Li5La3Nb2O12 (LLNO) is a typical garnet-like solid electrolyte with solitary cubic structure. However, its ionic conductivity is relatively low due to the low relative density when prepared by cold isostatic pressing method, which usually involves high-pressure machines, poor productivity, tedious pressing operations, and low density. In this paper, self-consolidation method is developed to sinter dense LLNO electrolyte. Although not any pressing operations are employed in the entire process, the relative density of LLNO is promoted up to 95%, which is much higher than the reported values of 45-80%. SEM images reveal that the sample is built by huge particles in size of 80 mu m indicating that there are few boundaries in the sample. Moreover, a rich content of Li-Al-O compounds is detected out in the boundary areas, which may act as sintering aids for the sample to consolidate automatically. According to the highest density, the bulk ionic conductivity of LLNO sample reaches up to 1.61 x 10(-4) S cm(-1) at 30 degrees C, which is in the same order of magnitude as the value of cubic Li7La3Zr2O12 electrolyte. This work verifies the self-consolidation mechanism for the sintering of ceramic electrolytes and could significantly facilitate the development of LLNO membrane technology.