The nascent morphology of UHMW PE exhibits high melting point, high crystallinity, and increased WAXS line breadth relative to samples formed by melt crystallization. Different empirical relationships between crystal size and melting point are observed for nascent and molded samples. This differentiation is removed following nitric acid treatment of the nascent flake. Solid-state annealing behavior is differentiated by several regimes. Regime I is characterized by increasing crystallite dimensions and crystallinity at low annealing temperatures. Regime II[a] and II[b] is identified by double melting in DSC scans of moldings and nascent flake, respectively. The double melting is due to partial melting with incomplete recrystallization. Regime II[a] of moldings is differentiated from Regime II[b] of flake by an increase in melting point of the higher melting endotherm. Within Regime II[b], the partial melting of the nascent structure is sensitive to the distribution of morphological stability. Regime LII is initiated at annealing temperatures approaching the zero heating rate melting point, and shows melting kinetics by DSC or time-resolved WAXS using synchrotron x-ray radiation. The superheat, partially associated with Regime III behavior, is sensitive to morphological heterogeneity and annealing history. Morphological models are discussed which highlight the role of noncrystalline regions and melting kinetics on the melting behavior of nascent form crystallinity.