Mn3O4/reduced graphene oxide/single-walled carbon nanotube flexible hybrid film with outstanding flexibility and electrochemical performance is prepared via a vacuum filtration method. The three-dimensional interconnect structure is constructed by reduced graphene oxide and single-walled carbon nanotube, and Mn3O4 nanoplates with pesudocapacitance are embedded into the interconnect structure. The regular interconnect structure and a synergetic effect between graphene oxide/single-walled carbon nanotube and Mn3O4 make the Mn3O4/reduced graphene oxide/single-walled carbon nanotube flexible film electrode exhibit a large areal capacitance of 796 mF cm(-2). All-solid-state Mn3O4/reduced graphene oxide/single-walled carbon nanotube flexible supercapacitor is prepared by using the hybrid film as electrodes and sandwiching the PVA-KOH gel electrolyte, it exhibits a large area specific capacitance of 360 mF cm(-2) and the capacitance maintains 95% after 5000 charge/discharge cycles. The assembled supercapacitor exhibits both outstanding mechanical performance and a high areal energy density of 32 mu Wh cm(-2) at an areal power density of 0.392 mW cm(-2). The Mn3O4/reduced graphene oxide/single-walled carbon nanotube flexible supercapacitors exhibit significant potentiality in flexible and wearable electronics owing to their excellent flexibility, high energy density and long cycle life. (C) 2018 Elsevier Ltd. All rights reserved.