Herein, we propose a facile incomplete phase separation strategy unlike the tedious synthesis approaches of the past to fabricate P/N co-doped porous and interconnected carbon (PNPC) particles with a specific surface area (S-A) of 1920 m(2) g(-1). The heteroatom doped porous carbons were demonstrated to possess improved conductive property and excellent stability for supercapacitor application. The PNPC bunch delivered a high specific capacitance of 318 F g(-1) at 1 A g(-1) and a remarkable cycling stability, i.e., 96.2% initial capacitance after 10,000 cycles in 6 M KOH electrolyte solution. In addition, an asymmetric supercapacitor (ASC) employing LaNi0.5Co0.5O3/0.333Co(3)O(4) hollow spheres with a mesoporous shell as a positive electrode and PNPC bunch as a negative electrode showed a maximum specific capacitance of 109.6 F g(-1) at 1 A g(-1) in a potential window of 0-1.7 V. More importantly, the reformative ASC can be discharged up to 0.5 s at a charge current density of 1 A g(-1) to deliver an ultrahigh power density of 89.7 kW kg(-1), much higher than those of the reported ASCs. This exciting result paves a way for practical application in high power devices. (C) 2018 Elsevier Ltd. All rights reserved.