With a notable advantage in terms of specific capacity (1166 mAh g(-1)), lithium disulfide (Li2S) has been considered a promising cathode material for high-energy-density lithium-sulfur (Li-S) batteries. In contrast to pure sulfur, Li2S opens the opportunity to implement alternative anodes such as silicon or graphite instead of hardly controllable lithium metal. However, its intrinsically low conductivity and the formation of soluble lithium polysulfide species during cell operation resulting in a poor cycling stability, especially in carbonate-based electrolytes. Herein, a reduced graphene oxide-wrapped Li2S particles (Li2S@rGO) electrode is presented for improving the electrochemical performance of Li-S batteries in carbonate-based electrolytes. A hydrothermally prepared rGO-covered MoS 2 particles composite was fully lithiated and irreversible decomposed at 0.01 V vs. Li/Li+ to in situ produce a Li2S@rGO composite with a high Li2S loading of approximate to 5 mg cm(-2). Despite operating Li-S cells in a conventional carbonate-based electrolyte, the resulting cathode exhibits high initial capacity (975 mAh g(Li2S)(-1) and 1401 mAh g(s)(-1) at 0.1 C), low degradation rate (0.18% per cycle after 200 cycles at 2 C) and excellent Coulombic efficiency ( approximate to 99.5%). This work provides a simple strategy to fabricate practical high-loading Li2S cathodes for high- performance Li-S batteries "free" of polysulfide shuttle phenomenon. (C) 2018 Elsevier Ltd. All rights reserved.