Photodriven nonoxidative coupling of CH4 (NOCM) is a potential alternative approach to clean hydrogen and hydrocarbon production. Herein, a Mott-Schottky photocatalyst for NOCM is fabricated by loading Pt nanoclusters on a Ga-doped hierarchical porous TiO2-SiO2 microarray with an anatase framework, which exhibits a CH4 conversion rate of 3.48 mu mol g(-1) h(-1) with 90% selectivity toward C2H6. This activity is 13 times higher than those from microarrays without Pt and Ga. Moreover, a continuous H-2 production (36 mu mol g(-1)) with a high CH4 conversion rate of similar to 28% can be achieved through a longtime irradiation (32 h). The influence of Ga on the chemical state of a surface oxygen vacancy (Vo) and deposited Pt is investigated through a combination of experimental analysis and first-principles density functional theory calculations. Ga substitutes for the five-coordinated Ti next to Vo, which tends to stabilize the single-electron trapped Vo and reduce the electron transfer from Vo to the adsorbed Pt, resulting in the formation of a higher amount of cationic Pt. The cationic Pt and electron-enriched metallic Pt form a cationic-anionic active pair, which is more efficient for the dissociation of C-H bonds. However, the presence of too much cationic Pt results in more C2+ product with a decrease in the CH4 conversion rate due to the reduced charge-carrier separation efficiency. This study provides deep insight into the effect of the doping/loading strategy on the photocatalytic NOCM reaction and is expected to shed substantial light on future structural design and modulation.