High capacity all-solid-state Li-ion battery anodes were prepared using an industrially scalable solution coating process. Employing commercially available polyacrylonitrile as amixed conducting binder, we have demonstrated stable cycling, high capacity electrodes with large mass loadings of tin active material. This is, to our knowledge, the first time a high capacity lithium-alloying material has been utilized in a slurry-coated sheet-style all-solid-state Li-ion battery anode. Optimization of this new electrode architecture resulted in a sheet-style anode capable of retaining an electrode specific capacity of 643.5 mAh/g after 100 charge-discharge cycles at a 0.1C rate. We believe that this work represents a step forward for slurry-coated electrodes intended for use with sulfide solid electrolytes and that the continued development of these high capacity sheet-style anodes will be critical to the commercialization of the all-solid-state Li-ion battery. (C) 2019 The Electrochemical Society.